Calcium phosphate and calcium carbonate mineralization of bioinspired hydrogels based on β-chitin isolated from biomineral of the common cuttlefish (Sepia officinalis, L.)

Abstract

Chitin, a bioactive, antibacterial and biodegradable polymer is commonly utilized by diverse marine organisms as the main scaffold material during biomineralization. Due to its properties, chitin is also of interest as a component of organo-inorganic composites for diverse biomedical applications. In this study, chitinous fibers isolated from the cuttlebone of the common cuttlefish (Sepia officinalis, L.) are characterized and evaluated for use as an integral part of mineralized hydrogels for biomedical applications. Since marine organisms use calcium carbonates (CaCO3), while vertebrates use calcium phosphates (CaP) as the main inorganic hard tissue components, and both minerals are used in hard tissue engineering, they were compared to determine which composite is potentially a better biomaterial. Hydrogel mineralization was conducted by subsequent dipping into cationic and anionic reactant solutions, resulting in the formation of a CaCO3 or CaP coating that penetrated into the hydrogel. Obtained composites were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), atomic force microscopy (AFM), scanning electron microscopy (SEM), rheology, swelling tests and simple compression. The results indicate that β-chitin can be used for the preparation of moldable hydrogels that are easily mineralized. Mineralized hydrogels have higher elasticity than non-mineralized ones while swelling is better if the extent of mineralization is lower. Further optimization of the hydrogels composition could improve their stress response and Young’s modulus, where the current hydrogel with a higher extent of CaP mineralization excels in comparison to all other investigated composites. © 2018, Springer Nature B.V.