Electrorheological properties of suspensions of hollow globular titanium oxide/polypyrrole particles

Abstract

Hollow globular clusters of titanium oxide (TiO(2)) nanoparticles were synthesized by a simple hydrothermal method. The prepared particles were consequently coated by in situ polymerization of conductive polymer polypyrrole (PPy) to obtain novel core-shell structured particles as a dispersed phase in electrorheological (ER) suspensions. The X-ray diffraction analysis and scanning electron microscopy provided information on particle composition and morphology. It appeared that PPy coating improved the compatibility of dispersed particles with silicone oil which results in higher sedimentation stability compared to that of mere TiO(2) particles-based ER suspension. The ER properties were investigated under both steady and oscillatory shears. It was found that TiO(2)/PPy particles-based suspension showed higher ER activity than that of mere TiO(2) hollow globular clusters. These observations were elucidated well in view of their dielectric spectra analysis; a larger dielectric loss enhancement and faster interfacial polarization were responsible for a higher ER activity of core-shell structured TiO(2)/PPy-based suspensions. Investigation of changes in ER properties of prepared suspensions as a function of particles concentration, viscosity of silicone oil used as a suspension medium, and electric field strength applied was also performed.